多束系统对12Cr-ODS钢辐照损伤协同效应的研究

张艳文; 刘士毅; 王绪; 王承; 赵子强; 钱晰; 李婷; 陆道纲

doi:null

您当前的位置：

首页 >

文章列表页 >

多束系统对12Cr-ODS钢辐照损伤协同效应的研究

低能加速器技术、射线技术及应用 | 更新时间：2021-03-05

- 多束系统对12Cr-ODS钢辐照损伤协同效应的研究
- Synergy effect of radiation damage on 12Cr-ODS steel by multi-ion-beams
- 核技术 2012年35卷第7期
- 作者机构：
  
  1. 北京大学重离子物理研究所核物理与核技术国家重点实验室
  2. 华北电力大学核科学与工程学院
- 作者简介：
- 基金信息：
  
  (No.ZX069)
- DOI：
  中图分类号： TL341
- 纸质出版日期：2012-07-01
- 稿件说明：
移动端阅览
[1]张艳文,刘士毅,王绪,王承,赵子强,钱晰,李婷,陆道纲.多束系统对12Cr-ODS钢辐照损伤协同效应的研究[J].核技术,2012,35(07):503-506.

ZHANG Yanwen1 LIU Shiyi1 WANG Xu1 WANG Cheng1 ZHAO Ziqiang1 QIAN Xi2 LI Ting2 LU Daogang2 1. Synergy effect of radiation damage on 12Cr-ODS steel by multi-ion-beams[J]. Nuclear techniques, 2012, 35(7): 503-506.
[1]张艳文,刘士毅,王绪,王承,赵子强,钱晰,李婷,陆道纲.多束系统对12Cr-ODS钢辐照损伤协同效应的研究[J].核技术,2012,35(07):503-506. DOI：

ZHANG Yanwen1 LIU Shiyi1 WANG Xu1 WANG Cheng1 ZHAO Ziqiang1 QIAN Xi2 LI Ting2 LU Daogang2 1. Synergy effect of radiation damage on 12Cr-ODS steel by multi-ion-beams[J]. Nuclear techniques, 2012, 35(7): 503-506. DOI：

摘要

室温下用不同种类的离子束对12Cr-ODS钢进行辐照。辐照前后12Cr-ODS钢的力学性能发生了明显变化

主要表现为辐照肿胀和辐照硬化

其中三束辐照下材料有最大的肿胀和最小的硬化。结合TEM照片对材料的辐照变化进行了分析。对材料进行拉曼光谱的测量

发现有碳析出现象

并且把碳峰的强度分布与辐照损伤分布进行了相互关联。本文为12Cr-ODS钢在实际反应堆中的应用积累了实验数据

明确了协同作用对核材料辐照损伤的影响。

Abstract

In this work

12Cr-ODS steel samples were irradiated by different combinations of Si

He and H ion beams at room temperature.Mechanical property measurements of the irradiated samples showed that all the samples exhibited irradiation swelling and hardening

but the sample co-irradiated by three ion beams had the biggest swelling and smallest hardening.Combining on the TEM imaging

analyses of irradiation changes of 12Cr-ODS steel samples were carried out.Raman spectra of the irradiated samples revealed carbon precipitated inside the samples

and carbon peak distribution could reflect the radiation damage distribution.The results

which accumulated experimental data and clarified the radiation damage to nuclear materials by synergy effect

are of help for application of 12Cr-ODS steel in an advanced reactor.

关键词

Keywords

references

浏览量

112

下载量

CSCD

文章被引用时，请邮件提醒。

提交

工具集

关联资源

NaI闪烁体的快中子辐照损伤

两类钒基合金的辐照硬化研究

低能氦离子辐照对钨和钼材料的表面损伤作用

辐照温度对钨材料表面微结构的影响

基于多模式扫描探针显微镜技术分析碳化硅的辐照损伤